Laminating Resins

Axson Surface and Gel Coats

Product	Description	Color	Applications	Pot Life	Shore Hardness	Density (g/cc)	Mix Ratio	Demold Time	Viscosity (cps)	Tg (°F)
Epoxy Surface Coats. Can be Sanded or Polished.
AS2003-1	Excellent edge coverage, no sag on vertical surfaces, easy to apply	White	Master models, trim fixtures, keller models, patterns and core boxes	25 min	83D	1.19	100 to 16	12 hr	40000	164
AS2020	High temperature resistance, no sag on vertical surfaces. Aluminum filled	Gray	Fillets and reinforcements, laminating in production molds	60 min	92D	1.52	100 to 11	12 hr	Thixotropic	310
S11	Bonds to wet plaster and concrete, heat resistant, high gloss finish	White	Plastic faced plaster, thermoplastic sheet forming molds, spotting racks	15 min	88D	1.22	100 to 16	8 hr	Thixotropic	200
S20	Chemical resistant, applies easily, excellent finish, high Shore hardness	Red	Surface coating of molds requiring chemical and heat resistance	35 min	90D	1.46	100 to 16	16 hr	Thixotropic	275
Polyester Gel Coats for Specific Applications
APF 1700	Sprayable, rapid layer build up when applied in thin coats, impact resistant	Light Gray	Master mold surfacing, preparation or surface repair of molds	25 min	88D	1.4	100 to 2	1 hr	Sprayable	400
APG 1750 S	Sprayable high temperature gel coat, high gloss finish	Orange	Creation of high gloss mold surfaces, high heat and impact resistance	10 min	88D	1.4	100 to 2	1 hr	Sprayable	400

Axson Laminating Resins

Product	Description	Color	Applications	Pot Life	Shore Hardness	Density (g/cc)	Mix Ratio	Demold Time	Viscosity (mPa.s.)	Tg (°F)
AL2103	Low/No vertical sag, room temperature cure, low toxicity, good dimensional stability	White	Use with glass or organic fabrics, laminating and bonding	20 min	85D	1.33	100 to 16	12 hr	3000	132
AL2103 LPL		White	Use with glass or organic fabrics, laminating and bonding	30 min	95D	1.26	100 to 16	24 hr	2000	146
AL2108	Thin film cure, clear, fast wetting	Clear	Master models, trim fixtures, duplication splashes, back fill, patterns, core boxes	25 min	85D	1.1	100 to 25	10 hr	1000	154
AL2120	Aluminum filled, high temperature laminating system for tooling	Light Gray	Vacuum forming tools, autoclave tools, high temperature bonding fixtures	60 min	82D	1.27	100 to 16	24 hr	5500	248
Eoplam 2015
2014	Designed for the production of composite structures by wet layup methods	Clear	Wood impregnation, vacuum bagging, filament winging, resin transfer molding	60 min	83 D	1.12	100 to 32	24 hr	650	196
2015				140 min	82D	1.08		30 hr	550	190
2016				400 min	84D	1.14		48 hr	450	178
Epolam 2017 / 2019	High performance laminating system for vacuum bagging with heated cure, long open time, quick demold	Clear	Composite automotive bodies by vacuum bagging, resin transfer molding	3 hr 35 min	84D	1.14	100 to 32	24 hr	1080	178
Epolam 2020	Curing time controlled by adding accelerators, low viscosity, good wetting	Clear	Very best composite parts, wet layup, resin transfer molds	2 hr 15 min	85D	1.1	100 to 34	48 hr	500	176
Epolam 2022	Heat resistant unfilled laminating system	Clear	Vacuum bagging, filament winding, resin transfer molding, resin infusion	60 min	85D	1.1	100 to 40	24 hr	5400	212
Epolam 2025	Heat resistant unfilled laminating system well suited for thick sections	Translucent yellow	Vacuum bagging, filament winding, resin transfer molding, composite tooling	70 min	87D	1.12	100 to 28	24 hr	1300	275
Epolam 2025L		Translucent yellow		110 min	87D	1.16	100 to 33	24 hr	1800	275
Epolam 2500	Self-extinguishing, FAR25.653 approved, fast and slow hardeners available	Off White	Fire resistant composites for aircraft interiors	1 hr 20 min	88D	1.2	100 to 22	16 hr	3500	212
Epolam 2501		Off White	Fire resistant composites for aircraft interiors	25 min	89D	1.2	100 to 18	4 hr	1800	199
RSF 816	Transparent, fast setting, low viscosity laminating system with UV resistance	Clear	Designed for producing surfboards or any transparent top coated laminate by wet layup methods	25 min	82D	1.15	100 to 40	16 hr	500	176
Infusion Resins
Epolam 2035/
2025	Intermediate elevated temperature infusion system with 2 set times	Clear	Production of composite tooling by infusion for temperatures to 265°F	105 min	83D	1.12	100 to 27	24 hr	400	266
2025L		Clear		165 min	83D	1.12	100 to 31	48 hr	500	266
Epolam 2090/ 2026	Low viscosity system designed for the production of high temperature tooling by infusion	Translucent Amber	Production of very large tools for high heat applications - 360°F at 90 psi	25 hr	90D	1.14	100 to 53	12 hr heat cure needed	650	400
Epolam 5015/
5014	Very low viscosity infusion system, excellent wetting properties	Translucent	Production of large parts, boat hulls, wind turbine blades	45 min	82D	1.12	100 to 34	18 hr	225	176
5015				2 hr 15 min	84D	1.1	100 to 30	24 hr	210	180
5016				3 hr 45 min	83D	1.12	100 to 36	48 hr	225	179
Laminating Pastes
Epopast 206	Heat resistant, dimensionally stable, low density	Blue	Large negatives, tooling for composites and vacuum castings	1 hr 25 min	70D	0.91	100 to 12	20-24 hr	Paste	258
Epopast 206 Coupling Layer Kit		A combination of a heat resistant laminating resin with chopped fiberglass strand and thixotropic filler. Use as an intermediate layer between the surface coat and Epopast 206. Reduces defects in tool construction
Epopast 400	Low shrinkage, low odor, easy to mix and apply.	Green	Large negatives, inspection jigs, ceramics tooling, core boxes	2 hr	80D	0.91	100 to 14	24 hr	Paste	158
Epopast 402	Low shrinkage, low odor, easy to mix and apply.	Green	Large negatives, inspection jigs, ceramics tooling, lower density and less abrasive than Epopast 400	2 hr	81D	0.76	100 to 14	24 hr	Paste	158
Epopast 400 Coupling Layer Kit		A combination of a room temperature laminating resin with chopped fiberglass strand and thixotropic filler. Use as an intermediate layer between the surface coat and Epopast 400 or Epopast 402. Reduces defects in tool construction