Prototyping Resins
Axson Vacuum Casting Resins
|
Product |
Description |
Color |
Applications |
Pot Life |
Shore Hardness |
Density (g/cc) |
Flexural Modulus (PSI) |
Elongation at Break (%) |
Mix Ratio |
Demold Time @ 70°C |
Tg (°F) |
|
Rigid Casting Resins |
|||||||||||
|
PX223HT |
Low viscosity, impact resistant, high temperature resistance |
Black |
Similar to ABS |
7 min |
80D |
1.14 |
333,500 |
11 |
100 to 80 |
45 min |
248 |
|
PX226 |
Very short demold time, low viscosity |
White |
Similar to filled ABS or PA 6.6 |
4 min |
82D |
1.2 |
362,500 |
15 |
100 to 50 |
25min |
221 |
|
PX226L |
7.5 min |
60 min |
|||||||||
|
PX234HT |
Extremely high temperature resistance |
Light Amber |
Similar to PA 66, PPS, PEEK |
4 min |
80D |
1.19 |
268,250 |
13 |
100 to 50 |
60 min |
410 |
|
PX 245 |
Filled, very short demold time, very rigid |
White |
Similar to P.O.M. and filled thermoplastics |
4 min |
85D |
1.22 |
652,500 |
3 |
100 to 40 |
30 min |
203 |
|
PX245L |
8 min |
60 min |
|||||||||
|
PX330 |
Fire retardant, meets FAR 25.853 |
Gray |
Technical parts for aeronautics, parts where fire certification is needed |
5min |
87D |
1.33 |
478,500 |
3 |
100 to 100 |
45 min |
220 |
|
PX521HT |
Low Viscosity, high heat resistance |
Clear |
Polycarbonate, glass or crystal, PMMA |
20 min |
87D |
1.06 |
304,500 |
10 |
100 to 55 |
2 hrs |
230 |
|
PX522HT |
7 min |
45 min |
|||||||||
|
Semi-Rigid Casting Resins |
|||||||||||
|
PX100 |
Low viscosity, hand castable |
White |
Polystyrene, polypropylene, prototype parts like H.I.P.S. |
15 min |
74D |
1.16 |
217,500 |
20 |
100 to 100 |
4 hr |
167 |
|
PX205 |
Unbreakable, living hinge effect |
Off White |
Polypropylene |
14 min |
70D |
1.08 |
72,500 |
100 |
100 to 50 |
1 hr |
203 |
|
PX212 |
Low viscosity, fast demold time, impact resistant |
Clear |
Polypropylene, Ideal for rotomolding applications |
5min |
76D |
1.15 |
174,000 |
25 |
100 to 100 |
1hr 10min |
194 |
|
Flexible Casting Resins |
|||||||||||
|
PX761 |
High heat resistance, long pot life |
Amber |
Rubber like prototype parts |
10 min |
63A |
1.03 |
|
1,000 |
100 to 45 |
1hr 30min |
|
Axson Reaction Injection Molding (RIM) Resins
|
Product |
Description |
Color |
Applications |
Pot Life (sec.) |
Shore Hardness |
Density (g/cc) |
Flexural Modulus (PSI) |
Mix Ratio |
Demold Time |
Tg (°F) |
|
Multi-Use RIM |
||||||||||
|
RIM 610 |
Fire retardant, UL 94-VO, ABS-like |
White |
Suitable for electrical housings |
50-70 |
80D |
1.29 |
305,000 |
100 to 100 |
20 min |
221 |
|
RIM 826/902 |
Very high impact resistance, easy to use |
Black |
High impact resistant prototypes |
10-100 |
73D |
1.12 |
116,000 |
100 to 100 |
25 min |
203 |
|
RIM 880 |
Neutral color, polycarbonate properties |
Tan |
Easily tinted, sag-free post cure, fast demold |
60-80 |
84D |
1.14 |
329,000 |
100 to 100 |
7 min |
201 |
|
Blendable Polyols for Adjustable Properties |
||||||||||
|
RIM 875 |
High impact resistance, polyol can be mixed to obtain intermediate stiffness |
Black |
Prototype parts, polypropylene, polyethylene appearance |
60-80 |
75D |
1.12 |
145,000 |
100 to 80 |
15 min |
212 |
|
RIM 876 |
Prototype parts, ABS / polystyrene appearance |
60-70 |
80D |
290,000 |
100 to 100 |
|||||
|
RIM 975 |
High impact resistance, polyol can be mixed to obtain intermediate stiffness |
Black |
Prototype parts, small runs, polypropylene / polyethylene appearance |
38-42 |
75D |
1.2 |
145,000 |
75 to 100 |
5 min |
302 |
|
RIM 976 |
Prototype parts, ABS / polystyrene appearance |
35-40 |
80D |
1.19 |
290,000 |
100 to 100 |
10 min |
|||